Influence of proton irradiation on the magnetic properties of two

Aug 15, 2023

Scientific Reports volume 13, Article number: 14032 (2023) Cite this article

900 Accesses

Metrics details

The influence of 1.9 MeV proton irradiation on structural and magnetic properties has been explored in the two-dimensional (2D) NiSO4(1,3-phenylenediamine)2 coordination ferrimagnet. The X-ray powder diffraction and IR spectroscopy revealed that the octahedrons with Ni ion in the center remain unchanged regardless of the fluence a sample received. In contrast, proton irradiation greatly influences the hydrogen bonds in the flexible parts in which the 1,3-phenylenediamine is involved. Dc magnetic measurements revealed that several magnetic properties were modified with proton irradiation. The isothermal magnetization measured at T = 2.0 K varied with the proton dose, achieving a 50% increase in magnetization in the highest measured field µ0Hdc = 7 T or a 25% decrease in remanence. The most significant change was observed for the coercive field, which was reduced by 90% compared to the non-irradiated sample. The observed results are accounted for the increased freedom of magnetic moments rotation and the modification of intralayer exchange couplings.

The recent intensive investigations in the field of multifunctional molecular materials are integrally related to their possible application in modern technology, such as high-density data storage and processing1,2,3,4, magnetic refrigeration5,6,7,8, or optically active sensors and switches9,10. The broad capability of molecular magnetism emerges from the variety of available structures11,12 and the possibility of changing their properties with external stimuli, including temperature, pressure13, and light irradiation14. Proton irradiation is another approach for tuning material properties by external factors. It is currently widely employed in the studies of carbon allotropes15,16, semiconductors17, films18, superconductors19, and alloys20 to engineer material features in a controllable manner21,22,23,24. Solids irradiated with energetic particles are exposed to extremely high-density local energy deposition that causes nonlinear and threshold effects25. As a result, new materials with novel properties can be obtained.

In particular, ion irradiation is used to modify magnetic properties. The induced defects may give rise to paramagnetic response in non-magnetic materials when the defect concentration exceeds a specific threshold value26,27,28 or alter the magnetic properties of paramagnets and systems with long-range magnetic order (LRMO), especially when strong magnetostructural correlations are present. The irradiation can increase Curie temperature29,30,31 and impact such properties as the coercive field, magnetization saturation, g-factor, and shape of the magnetic hysteresis loop32,33,34. Proton irradiation can generate changes at the atomic level over the selected area and depth by adjusting protons energy, which makes this approach perspective for the controlled engineering of magnetic materials29.

Currently, there are no systematic studies on the response of molecular magnetic materials to ion irradiation. To fill this gap, we examined the effects of 1.9 MeV proton irradiation on the magnetic properties of the NiSO4(1,3-phenylenediamine)2 coordination polymer, hereafter abbreviated as Ni(MPD)2SO4. This molecular magnet reveals a considerable size of the coercive field and long-range magnetic ordering below TC = 24 K. X-ray powder diffraction, infrared spectroscopy, and magnetic measurements were performed to investigate the influence of proton fluence ϕ = 5 × 1013–2.2 × 1015 cm−2 on structural and magnetic properties. Although structural changes were observed only within the polymer part related to the C–H and N–H bonds, the proton irradiation has induced significant modifications of magnetic properties, especially the coercive field, degree of irreversibility, and maximum magnetization.

The Ni(MPD)2SO4 (Fig. 1) crystallizes in a monoclinic crystal system (Cc space group). The nickel (II) ions are bridged by tetrahedral \({\text{SO}}_{4}^{2 - }\) anions forming 2D layers parallel to the bc plane, and each layer is separated from one another by the 1,3-phenylenediamine (MPD) ligand. The nickel atom occupies the center of a distorted octahedron formed by two nitrogen atoms from the diamine molecules (MPD) and four oxygen atoms from three \({\text{SO}}_{4}^{2 - }\) anions. Each Ni2+ possesses six Ni2+ nearest neighbors and is separated from them by a distance of 4.914 Å, 4.931 Å, or 6.546 Å (two of each). The interlayer Ni–Ni distance is equal to 14.559 Å. More details regarding Ni(MPD)2SO4 structure were described in35. The XRPD measurements of all samples have not shown meaningful changes in the diffraction patterns pointing to the conservation of the Ni(MPD)2SO4 core structure after proton irradiation (see Supplementary Information Figure S1 online). However, greater half-widths of the diffraction peaks after proton irradiation may indicate the increase in crystal lattice microstrains or crystallites size reduction.

The crystal structure of Ni(MPD)2SO4: (a) representative molecular fragment (b) packing. Colors: Ni (green), S (yellow), O (red), C (black), N (light blue). Hydrogen atoms are omitted for clarity.

In the mid-infrared range, the absorption spectra observed for Ni(MPD)2SO4, for samples irradiated with various fluences, have complex character (see Fig. 2). In the range of the deformation vibrations (ν < 2000 cm−1), a series of δC–H bands (in a ring), overlapping with those originating from SO4 ions, are visible. The IR spectra show NiSO4 sharp peaks of the characteristic S–O stretch [νS–O(SO4) 900–1500 cm−1] and deformation [δS–O(SO4) 400–700 cm−1] vibrations. On the other hand, a band corresponding to the stretching vibration from the Ni = O group is visible at about 600 cm−1. Broad bands, corresponding to S–O vibrations in the SO4 atomic group, were observed at about: ~ 525 cm−1 as δS–O deformation vibrations, and ~ 1100 cm−1 and ~ 1600 cm−1 as νS–O stretching vibrations36.

Fourier-transform infrared spectroscopy (FTIR) patterns of the Ni(MPD)2SO4 samples irradiated with various fluences.

Vibration bands of the lighter atoms, i.e., C–H and N–H in MPD ligand, both deforming, i.e., in the range of 500 – 2000 cm−1, and the range of stretching vibrations, i.e., above 2000 cm−1, strongly overlap with the vibrations of the groups containing heavy atoms. They are visible in the form of low-intensity bands emerging from wide bands corresponding to the vibrations of the group, e.g., SO4. Bands at about (~ 700, ~ 1551) cm−1 are assigned to the vibrations of the CN group37.

The range of stretching vibrations deserves special attention. The broad band in this range (νCH, νNH) becomes asymmetric with the increase of the irradiation dose. The band is shifted towards a higher wavenumber (blue shift) which means that the strengths of the C–H and N–H are weakened38. The C–H and N–H bonds are involved well in forming hydrogen bonds, and the molecule's structure (shown in Fig. 1) perfectly enables it. A substantial change in the shape of the band with increasing irradiation dose proves the considerable influence of the hydrogen bonds on the ordering of the structure in its flexible parts in which MPD is involved.

Moreover, the visible asymmetry of the band indicates that there are different types of hydrogen bonds in which the nitrogen atom is involved. The nitrogen atom from the molecule's core (close to the nickel atom) is very stable (rigid) due to its involvement in covalent bonds. In contrast, the steric conditions for the "free" nitrogen atom favor the rapid formation/breaking of intermolecular bonds. Therefore, these weak interactions only affect the elastic part of the molecules, while the core of the molecule does not feel their presence. The assignments of major vibrational bands in the FTIR spectra of the Ni(MPD)2SO4 samples irradiated with various fluences are in Table 1.

The general magnetic properties of Ni(MPD)2SO4 were investigated in the recent work by González Guillén et al.35. Three magnetic couplings were found in the system: two competing intralayer superexchange pathways, antiferromagnetic and ferromagnetic, that lead to non-collinear ordering within a layer and a dipole–dipole coupling between layers. The low anisotropy of Ni(II) ions does not promote 2D long-range magnetic ordering (LRMO). Therefore, the LRMO occurs below the Curie temperature TC = 24 K when all three interactions (where the dipolar coupling is the weakest one) are strong enough to couple magnetic moments in 3D. The product of molar magnetic susceptibility and temperature χT of Ni(MPD)2SO4 measured in the temperature range T = 2.0 – 300 K in a constant magnetic field of µ0Hdc = 0.05 T is shown in Fig. 3. At T = 300 K, χT equals 1.18 emu·K·mol−1, which can be obtained for a single isolated NiII ion with spin SNi = 1, assuming a spectroscopic factor g = 2.17. Such enhancement of g is expected for the NiII ion placed in the octahedral ligand field39.

Temperature dependence of χT product for Ni(MPD)2SO4 reference sample in the static magnetic field of µ0Hdc = 0.05 T.

The field cooling (FC) and zero-field cooling (ZFC) magnetic susceptibilities of Ni(MPD)2SO4 as a function of temperature are shown in Fig. 4 for proton fluences ranging from ϕ = 0 cm−2 to ϕ = 2.2 × 1015 cm−2. The temperature of phase transition to LRMO obtained from the temperature derivatives of FC and ZFC curves was TC = 24 K regardless of the sample radiation dosage. Compared to the reference sample, an additional increase in susceptibility was observed at the lowest temperatures for the samples irradiated with protons. However, the overall shapes of FC/ZFC were preserved above about T = 5.0 K. The obtained susceptibility magnitude varied between each sample; for the FC mode, from 90 to 130% of the reference sample’s corresponding value, whereas for ZFC, it varied between 55 and 170%. The largest FC/ZFC signal was obtained for ϕ = 2.5 × 1014 cm−2 and the lowest for ϕ = 1014 cm−2. The former sample was also the only one for which the FC/ZFC values above T = 5.0 K were greater than the values for the reference sample.

Field cooling (FC–full points) and zero-field cooling (ZFC – empty points) magnetic susceptibilities of Ni(MPD)2SO4 samples irradiated with various fluences ϕ measured in static magnetic field µ0Hdc = 0.01 T at T = 2.0–50 K.

The pair of ZFC and FC curves coincide with each other only above a certain irreversibility temperature Tirr40, which can be found by plotting the difference between FC, χFC(T), and ZFC, χZFC(T), susceptibilities, and determining the temperature above which the difference becomes less than 5%. The degree of irreversibility Δχirr was estimated for each studied fluence using the following integral41:

where T1 = 2.0 K and T2 = Tirr.

The Tirr and ∆χirr are summarized in Fig. 5 for each irradiation dose. The Tirr weakly depends on the irradiation dose revealing values between 23 and 25 K, corresponding to 105–115% of the reference sample’s Tirr. However, proton irradiation has a stronger influence on the degree of irreversibility. The obtained values of Δχirr, between 2.4 emu·mol−1·K and 2.95 emu·mol−1·K, are from 115 to 140% of the reference sample’s Δχirr. The highest Tirr = 25 K was found for ϕ = 2.2 × 1015 cm−2, while the maximal value of Δχirr = 2.95 emu·mol−1·K was for ϕ = 1014 cm−2.

The degree of irreversibility Δχirr (1) (left axis) and irreversibility temperature Tirr (right axis) for Ni(MPD)2SO4 samples irradiated with various fluences. The dashed lines represent the values obtained for the reference sample ϕ = 0 cm−2 and dotted areas their errors.

The Fig. 6 shows the isothermal magnetization of Ni(MPD)2SO4 obtained at T = 2.0 K for all studied fluences ϕ. In µ0H = 7 T, the lowest value of magnetization M7T = 0.3 μB·mol−1 was observed for ϕ = 5 × 1013 cm−2 sample and the highest M7T = 0.65 μB·mol−1 for ϕ = 5 × 1014 cm−2 sample, compared to M7T = 0.45 μB·mol−1 for the reference sample (where M7T is the magnetization at µ0H = 7 T).

The isothermal magnetization of Ni(MPD)2SO4 samples irradiated with various fluences ϕ measured at T = 2.0 K and in applied magnetic fields from zero to µ0H = 7 T. Inset: the picture enlarged on µ0H = [− 0.2 T, 0.2 T] range to show the coercivity and remanence of the samples.

The low field part of magnetic hysteresis loops is depicted in the inset of Fig. 6, enlarged on the coercivity µ0Hc and remanence MR. The M(H) loops were opened below µ0H = 1 T for all the samples. The hysteresis loop for the sample with the lowest fluence of ϕ = 5 × 1013 cm−2 coincided with the reference’s loop in the field range µ0H = [− 1 T, 1 T]. For the remaining samples, the values of µ0Hc and MR were reduced, and a step in the M(H) loop near µ0H = 0 T appeared, which is especially visible for ϕ = 1014 cm−2. Figure 7. shows the hysteresis loop parameters for the irradiated samples, presented as a relative value to the reference sample’s coercivity (µ0Hc = 0.13 T), remanence (MR = 0.45 μB·mol−1), and magnetization at µ0H = 7 T (M7T = 0.3 μB·mol−1). M7T is reduced for ϕ = 5 × 1013 cm−2 to 65% of the reference level, but it raises with an increasing ϕ to 150% for ϕ = 2.5 × 1014 cm−2. The further increase in fluence reduces the value of M7T, which becomes 95% of the reference level for the sample with the highest studied fluence of ϕ = 2.2 × 1015 cm−2. The samples irradiated with the fluences ϕ ≥ 1014 cm−2 showed the reduction of µ0Hc to 10–55% and MR to 75–90% of the reference level.

The relative values of magnetic hysteresis loop parameters for Ni(MPD)2SO4 samples irradiated with various fluences ϕ normalized to the reference sample’s corresponding values. Violet stars: magnetization at µ0H = 7 T (M7T); red circles: coercive field (µ0Hc); green pentagons: remnant magnetization (MR). The dashed line is placed at 100% and represents the values obtained for the reference sample ϕ = 0 cm−2 with errors indicated by gray dotted area. The lines between points are only for an eye guide.

The XRPD and IR spectroscopy measurements indicated that the core structure of Ni(MPD)2SO4 remains unchanged. Consequently, the interlayer distance and the dipolar interaction are the same regardless of the fluence a sample received. Furthermore, the Curie temperature TC remains the same because its value is determined by the weakest magnetic coupling, the dipole–dipole one. On the other hand, irradiation significantly modifies the C–H and N–H bonds, which are involved in forming hydrogen bonds related to the MPD ligand (the flexible part of the structure). In particular, the interaction of lattice with protons may lead to the C–H and N–H bonds breakage, creating hydrogen vacancies that would not be visible in XRPD, as reported in the methylammonium lead iodide perovskites after 10 MeV proton irradiation42 or polymer composite of polymethyl methacrylate doped with ferric oxalate after 3 MeV proton irradiation43.

The bond modification leads to changes in the crystal field, incorporation of local defects, altered intralayer exchange couplings (due to local structure modification), and increased freedom of the magnetic moments. In consequence, magnetic properties in the LRMO phase (below TC) have been modified. Table 2. summarizes the influence of proton irradiation on the magnetic properties of Ni(MPD)2SO4.

The isothermal magnetization measurements (Fig. 6) confirm a strong influence of irradiation on the magnetization processes in Ni(MPD)2SO4. The main reason for this is the increasing number of defects with increasing fluence. Note that irradiating the samples with the selected fluences is not enough to obtain a homogenous distribution of produced defects, and the observed magnetization data may be a mixture of several defect-induced magnetic phases of Ni(MPD)2SO4 with well-localized clusters. Introducing defects lowers the magnetostatic energy to a minimum for the dose of ϕ = 1014 cm−2 (the lowest value of the coercive field). However, a further increase in the number of defects leads to stronger pinning effects, which increase the coercive field for doses ϕ > 1014 cm−2.

The mechanism of M7T modification is different and related to changes in magnetic couplings in the compound. For the lowest dose of ϕ = 5 × 1013 cm−2, antiferromagnetic interactions are more dominant over the ferromagnetic ones, which lowers the magnetization M7T down to 67% of the M7T for the reference sample. For intermediate doses of ϕ = 1014 cm−2 and ϕ = 2.5 × 1014 cm−2, the corresponding values are 141% and 148%, respectively, indicating the enhancement of ferromagnetic interactions, and for the maximum dose of ϕ = 2.2 × 1015 cm−2, the value of M7T is similar to that for the reference. Note that the calculated magnetization for the parallel alignment of NiII magnetic moments (SNi = 1) with a spin-only Landé factor of g = 2.1735,39 yields the magnetization saturation of MS = 2.17 µB·mol−1. Thus, the antiferromagnetic interactions are dominant in all studied samples.

Similar non-monotonic effects of proton irradiation are commonly found in the literature31,33,34,44,45,46. In the Ni48·4Mn28.8Ga22.8 film irradiated with 120 keV protons45, the MS for ϕ = 1015 cm−2 raised to 155% of the non-irradiated sample’s value, but for ϕ = 2 × 1016 cm−2, the observed MS was only 102%. Another case is the initially diamagnetic SiC (0001) single crystal44 that displays ferromagnetism after 3 MeV proton irradiation treatment. For ϕ = 8 × 1015 cm−2, the MS measured in-plane reached 0.17 emu·g−1 but for ϕ = 1.3 × 1016 cm−2 it was reduced to 0.09 emu·g−1.

An additional increase of the magnetization in the FC/ZFC curves observed at T = 2–6 K for all irradiated samples may arise from a small sample’s fraction, which due to the deformation and partial destruction of a lattice, leads to the creation of localized magnetic moments due to open bonds47 or paramagnetic amorphous zones in the lattice44. This paramagnetic contribution may also cause the appearance of the observed step in the hysteresis loop near-zero field. The other possibility is the chemical composition modification of Ni(MPD)2SO4 samples by incorporating the highly energetic hydrogen atoms into the crystal lattice44,45. However, no additional phases were detected in the XRPD and IR measurements. Therefore, the amount of paramagnetic phase is not significant.

In summary, we have investigated the impact of 1.9 MeV proton irradiation on the layered Ni(MPD)2SO4 molecular magnet in the function of received fluence ϕ. It was found that proton irradiation influences only the flexible part of the structure (related to the C–H and N–H bonds in the MPD ligand), while the core of the compound remains unchanged. These lead to significant changes in magnetic properties as a function of fluence: coercive field µ0Hc (reduction up to 90%), maximal magnetization M7T (between 65 and 150% of the reference sample), remanence MR (reduction up to 25%) and degree of irreversibility Δχirr (increase up to 40%). Simultaneously, the Curie temperature was constant TC = 24 K regardless of ϕ because the core structure, interlayer distance, and, consequently, dipolar coupling of the Ni(MPD)2SO4 system remains the same. The observed non-monotonic magnetic properties changes are caused by the altered intralayer exchange couplings due to local structure modification, incorporation of local defects, and increased freedom of the magnetic moments.

The studied Ni(C6H8N2)2SO4 compound (hereafter abbreviated as Ni(MPD)2SO4) was synthesized using NiSO4·7H2O and 1,3-phenylenediamine (MPD, C6H8N2) ligand with a solvent-free synthesis approach according to the literature procedure35.

The Van de Graaff accelerator was used to generate a proton beam with set conditions: energy of 1.9 MeV, particle current of 10–12 nA, and beam size of about 0.5 mm × 0.5 mm. Powder samples mounted on copper plates were used (see Supplementary Figure S2 online) with a thickness lower than the 1.9 MeV proton penetration depth (see Supplementary Figure S3 online). The obtained fluences were equal to: ϕ = 5 × 1013 cm−2, 1014 cm−2, 2.5 × 1014 cm−2, 2.2 × 1015 cm−2.

X-ray powder diffraction (XRPD) patterns were determined by the PANalytical X’Pert Pro instrument with a copper X-ray tube source (Cu K α1, 1.541 Å), operated at 40 kV and 30 mA in the θ–2θ geometry. Data were recorded at room temperature in the range of 5–40° 2θ. The results were adjusted by background correction and the anode’s characteristic X-ray Kα2 removal.

The infrared spectroscopy measurements were done for samples in powder form, pelleted with potassium bromide (transparent in the mid-infrared range). Fourier-transform infrared spectroscopy (FTIR) measurements were carried out in the mid-infrared range (4000–500 cm−1), with a resolution of 2 cm−1, on the EXCALIBUR 3000 spectrometer; 128 scans were done for the spectrum at room temperature.

The Quantum Design SQUID MPMS-XL magnetometer was used to measure the magnetic properties of all powder samples. The isothermal magnetization M(µ0H) was collected in the applied field of µ0H = [− 7 T, 7 T]. Static magnetic susceptibility measurements were carried out in the field cooling (FC) and zero-field cooling (ZFC) modes in the T = 2.0–300 K temperature range with the applied field of µ0Hdc = 0.01 T. The obtained data points were processed taking the whole sample mass, i.e., assuming a homogeneous distribution of potential changes in the studies compounds after proton irradiation. The temperature-independent diamagnetic contribution of χ0 =  − 1.84 × 10−4 emu·mol−1 estimated from Pascal’s constants48 was subtracted from the measured signals.

The datasets used and/or analyzed during the current study are available from the corresponding author on reasonable request.

Raman, K. V. et al. Interface-engineered templates for molecular spin memory devices. Nature 493, 509–513 (2013).

Article ADS CAS PubMed Google Scholar

Aguilà, D. et al. Heterodimetallic [LnLn’] lanthanide complexes: Toward a chemical design of two-qubit molecular spin quantum gates. J. Am. Chem. Soc. 136, 14215–14222 (2014).

Article PubMed PubMed Central Google Scholar

Pedersen, K. S. et al. Toward molecular 4f single-ion magnet qubits. J. Am. Chem. Soc. 138, 5801–5804 (2016).

Article CAS PubMed Google Scholar

Coronado, E. Molecular magnetism: From chemical design to spin control in molecules, materials and devices. Nat. Rev. Mater. 5, 87–104 (2020).

Article ADS Google Scholar

Song, T. Q. et al. Wheel-like Ln18 cluster organic frameworks for magnetic refrigeration and conversion of CO2. Inorg. Chem. 57, 3144–3150 (2018).

Article CAS PubMed Google Scholar

Zheng, X. Y., Kong, X. J., Zheng, Z., Long, L. S. & Zheng, L. S. High-nuclearity lanthanide-containing clusters as potential molecular magnetic coolers. Acc. Chem. Res. 51, 517–525 (2018).

Article CAS PubMed Google Scholar

Wang, W. M. et al. Large magnetocaloric effect and remarkable single-molecule-magnet behavior in triangle-assembled LnIII6 clusters. New J. Chem. 43, 16639–16646 (2019).

Article CAS Google Scholar

Konieczny, P. et al. Magnetic cooling: A molecular perspective. Dalt. Trans. 51, 12762–12780 (2022).

Article CAS Google Scholar

Korzeniak, T. et al. Chiral photomagnets based on Copper(II) complexes of 1,2-Diaminocyclohexane and Octacyanidomolybdate(IV) Ions. Inorg. Chem. 59, 5872–5882 (2020).

Article CAS PubMed Google Scholar

Jiang, W. et al. Switching single chain magnet behavior: Via photoinduced bidirectional metal-to-metal charge transfer. Chem. Sci. 9, 617–622 (2018).

Article CAS PubMed Google Scholar

Yue, Q. & Gao, E. Q. Azide and carboxylate as simultaneous coupler for magnetic coordination polymers. Coord. Chem. Rev. 382, 1–31 (2019).

Article CAS Google Scholar

Pedersen, K. S., Bendix, J. & Clérac, R. Single-molecule magnet engineering: Building-block approaches. Chem. Commun. 50, 4396–4415 (2014).

Article CAS Google Scholar

Vallone, S. P. et al. Giant barocaloric effect at the spin crossover transition of a molecular crystal. Adv. Mater. 31, 1–7 (2019).

Article Google Scholar

Bridonneau, N. et al. Direct evidence of a photoinduced electron transfer in diluted “molybdenum-copper” molecular compounds. Eur. J. Inorg. Chem. 2018, 370–377 (2018).

Article CAS Google Scholar

Makgato, T. N. et al. Magnetic properties of point defects in proton irradiated diamond. J. Magn. Magn. Mater. 413, 76–80 (2016).

Article ADS CAS Google Scholar

Esquinazi, P. et al. Induced magnetic ordering by proton irradiation in graphite. Phys. Rev. Lett. 91, 8–11 (2003).

Article Google Scholar

Kasper, C. et al. Influence of irradiation on defect spin coherence in silicon carbide. Phys. Rev. Appl. 13, 1 (2020).

Article Google Scholar

Yang, Z. P., Tan, C. L., Gao, Z. Y., Gao, Y. & Cai, W. Effect of proton irradiation on microstructural and magnetic properties of ferromagnetic Ni–Mn–Ga thin films. Thin Solid Films 632, 10–16 (2017).

Article ADS CAS Google Scholar

Ghigo, G. et al. Effects of proton irradiation on the magnetic superconductor EuFe2(As1-xPx)2. Supercond. Sci. Technol. 33, 94011 (2020).

Article Google Scholar

Patki, P. V., Wu, Y. & Wharry, J. P. Effects of proton irradiation on microstructure and mechanical properties of nanocrystalline Cu–10at%Ta alloy. Materialia 9, 100597 (2020).

Article CAS Google Scholar

Smith, K. A. et al. Effect of proton irradiation on anatase TiO2 nanotube anodes for lithium-ion batteries. J. Mater. Sci. 54, 13221–13235 (2019).

Article ADS CAS Google Scholar

Smith, K. A. et al. Effects of proton irradiation on structural and electrochemical charge storage properties of TiO2 nanotube electrodes for lithium-ion batteries. J. Mater. Chem. A 5, 11815–11824 (2017).

Article CAS Google Scholar

Dutta, T. et al. Non-destructive patterning of 10 nm magnetic island array by phase transformation with low-energy proton irradiation. Appl. Phys. Lett. 111, 1–6 (2017).

Article Google Scholar

Kim, S. et al. Nanoscale patterning of complex magnetic nanostructures by reduction with low-energy protons. Nat. Nanotechnol. 7, 567–571 (2012).

Article ADS CAS PubMed Google Scholar

Avasthi, D. K. & Mehta, G. K. Swift Heavy Ions for Materials Engineering and Nanostructuring (Springer Series in Materials Science (Springer), 2011).

Book Google Scholar

Esquinazi, P. D. et al. Defect-induced magnetism in nonmagnetic oxides: Basic principles, experimental evidence, and possible devices with ZnO and TiO2. Phys. Status Solidi Res. 257, 1900623 (2020).

Article ADS CAS Google Scholar

Zhou, R. W., Liu, X. C., Li, F. & Shi, E. W. Defects induced ferromagnetism in hydrogen irradiated 3C–SiC thin films. Mater. Lett. 156, 54–57 (2015).

Article CAS Google Scholar

Hassan, N. U. et al. Influence of ion beam irradiation on structural, magnetic and electrical characteristics of ho-doped AlN thin films. Surf. Rev. Lett. 24, 1–7 (2017).

Article Google Scholar

Matsushita, M., Matsushima, Y., Uruga, T., Ishigami, R. & Iwase, A. Effect of 50-keV proton irradiation on the magnetism of a Fe66Ni34 Invar alloy. J. Magn. Magn. Mater. 333, 13–17 (2013).

Article ADS CAS Google Scholar

Matsushita, M., Wada, H. & Matsushima, Y. Effects of fluence and fluence rate of proton irradiation upon magnetism in Fe65Ni35 Invar alloy. J. Magn. Magn. Mater. 394, 491–495 (2015).

Article ADS CAS Google Scholar

Kim, S. J., Lee, K. J., Jung, M. H., Oh, H. J. & Kwon, Y. S. Magnetocaloric effect in la (Fe0.89Si0.11)13 irradiated by protons. J. Magn. Magn. Mater. 323, 1094–1097 (2011).

Article ADS CAS Google Scholar

Jiang, X. D. et al. Influence of the interface on the magnetic properties of NiZn ferrite thin films treated by proton irradiation. Nucl. Instrum. Methods Phys. Res. Sect. B Beam. Interact. Mater. Atoms. 358, 1–5 (2015).

Article ADS CAS Google Scholar

Jeon, G. W., Lee, K. W. & Lee, C. E. High-energy proton-irradiation effects on the magnetism of the transition-metal dichalcogenide MoS2. J. Korean Phys. Soc. 76, 93–96 (2020).

Article ADS CAS Google Scholar

Mathew, S. et al. Magnetism in MoS2 induced by proton irradiation. Appl. Phys. Lett. 101, 102103 (2012).

Article ADS Google Scholar

González Guillén, A. B. et al. Tuning magnetic properties by crystal engineering in a family of coordination polymers based on Ni(II) sulphates. New J. Chem. 46, 14786–14792 (2022).

Article Google Scholar

Dijs, I. J., De Koning, R., Geus, J. W. & Jenneskens, L. W. Anhydrous zirconium(IV) sulfate and tin(IV) sulfate: Solid Lewis acid catalysts in liquid-phase hydro-acyloxy-addition reactions?. Phys. Chem. Chem. Phys. 3, 4423–4429 (2001).

Article CAS Google Scholar

Nakagawa, I. & Shimanouchi, T. Infrared spectroscopic study on the co-ordination bond-II. Spectrochim. Acta 18, 101–113 (1962).

Article ADS CAS Google Scholar

Yao, W., Yu, S.-H., Jiang, J. & Zhang, L. Complex wurtzite znse microspheres with high hierarchy and their optical properties. Chem. A Eur. J. 12, 2066–2072 (2006).

Article CAS Google Scholar

Pinkowicz, D. et al. Nature of magnetic interactions in 3D {[MII(pyrazole)4]2[NbIV(CN)8]·4H2O}n (M = Mn, Fe Co, Ni) molecular magnets. Inorg. Chem. 49, 7565–7576 (2010).

Article CAS PubMed Google Scholar

Dubiel, S. M. & Felner, I. On the magnetism of C14Nb(Fe89.4Al10.6)2 laves phase intermetallic compound. Epl 128, 27005 (2019).

Article ADS CAS Google Scholar

Dubiel, S. M., Felner, I. & Tsindlekht, M. I. Magnetic phase diagram of sigma-phase Fe55Re45 compound in the H-T coordinates. J. Appl. Phys. 126, 154 (2019).

Article Google Scholar

Shin, J. et al. Proton irradiation effects on mechanochemically synthesized and flash-evaporated hybrid organic–inorganic lead halide perovskites. Nanotechnology 33, 065706 (2022).

Article ADS CAS Google Scholar

Shah, S., Qureshi, A., Singh, N. L., Singh, K. P. & Ganesan, V. Modification of polymer composite by proton beam irradiation. Soft Mater. 6, 75–84 (2008).

Article CAS Google Scholar

He, X. et al. Irradiation-induced magnetic ordering in SiC: Experimental results and a density functional study. Appl. Phys. Lett. 103, 262409 (2013).

Article ADS Google Scholar

Yang, Z. P., Sun, B., Gao, Z. Y. & Cai, W. Surface modifications and tailoring magnetism in Ni48.4Mn28.8Ga22.8 films by 120 keV proton irradiation. Intermetallics 98, 106–114 (2018).

Article CAS Google Scholar

Liu, Y. et al. Towards diluted magnetism in TaAs. Phys. Rev. Mater. 1, 044203 (2017).

Article ADS Google Scholar

Stöffler, D., Drescher, M., de Jauregui, D. S., Gmeiner, J. & Dormann, E. Proton irradiation defects in (fluoranthene)2PF6. Phys. Lett. A 363, 317–321 (2007).

Article ADS Google Scholar

Bain, G. A. & Berry, J. F. Diamagnetic corrections and Pascal’s constants. J. Chem. Educ. 85, 532–536 (2008).

Article CAS Google Scholar

Download references

We thank O. Polit for assistance in part of the correct sample preparation. This work was supported by the Polish Minister of Education and Science (G. No.: DI2017 006047).

Institute of Nuclear Physics PAN, ul. Radzikowskiego 152, 31-342, Cracow, Poland

Dominik Czernia, Piotr Konieczny, Ewa Juszyńska-Gałązka, Marcin Perzanowski & Janusz Lekki

Research Center for Thermal and Entropic Science, Graduate School of Science, Osaka University, 1-1 Machikaneyamacho, Toyonaka, Osaka, 560-0043, Japan

Ewa Juszyńska-Gałązka

Faculty of Chemistry, Jagiellonian University, ul. Gronostajowa 2, 30-387, Cracow, Poland

Anabel Berenice González Guillén & Wiesław Łasocha

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

D.C.: study design, magnetic properties data collection, analysis, and interpretation, manuscript preparation; P.K.: data interpretation, manuscript preparation; E.J.G.: infrared spectroscopy data collection and analysis, manuscript preparation; M.P.: powder X-ray data collection and analysis; J.L.: proton irradiation; A.B.G.G. and W.Ł.: sample synthesis, structure details, manuscript revision.

Correspondence to Dominik Czernia or Piotr Konieczny.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Czernia, D., Konieczny, P., Juszyńska-Gałązka, E. et al. Influence of proton irradiation on the magnetic properties of two-dimensional Ni(II) molecular magnet. Sci Rep 13, 14032 (2023). https://doi.org/10.1038/s41598-023-41156-8

Download citation

Received: 28 March 2023

Accepted: 22 August 2023

Published: 28 August 2023

DOI: https://doi.org/10.1038/s41598-023-41156-8

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.